CAD Metal Stamping Part Aluminum Alloy Panel For Computer Sand Blasting Oxidation
Notebook metal panel products Material: AL5052 Surface treatment: sandblasting oxidation Usage: Electronic devices
- Overview
- Description
- Details
- Inquiry
- Related Products
High Light | CAD Metal Stamping Part DWG Metal Stamping Part AL6063 aluminium alloy panel | |
| Material | AL6063/ AL5052 Aluminum, Stainless Steel, SECC, Carbon Steel, SPTE | |
| Size | As Customer Require | |
| Thickness | 0.5~25mm | |
| Application | Customized | |
| Drawing Format | CAD/DWG ETC | |
| Color | Color | |
| Place of Origin | China Shenzhen | |
| Brand Name | TOPWELL | |
| Certification | ISO9001 | 2015 |
| Minimum Order Quantity | 1000pcs | |
| Price | USD3-5 per pcs | |
| Packaging Details | 32*23*17cm | |
| Delivery Time | 5-8 work days | |
| Payment Terms | T/T | |
| Supply Ability | 10000 pcs days |
Description
Aluminum alloy panel for computer Sand blasting oxidation
Scope
Aluminium alloy 6063 is a medium strength alloy commonly referred to as an architectural alloy.It is normally used in intricate extrusions.It has a good surface finish, high corrosion resistance, is suited to welding and can be easily anodised.Most commonly available as T6 temper, in the T4 condition it has good formability.
Application
This material is used for architectural applications, shop fittings, irrigation tubing, balustrading, window frames,3C cooling parts, Decorative metal panels,mechanical parts, automobile parts, outdoor fitness equipment. extrusions and doors.
Supplied Forms
1 Extrusions
2 Tube
3 sheet material
Alloy Designations
Aluminium alloy 6063/6063A also corresponds to: AA6063, Al Mg0.7Si, GS10, AlMgSi0.5, A-GS, 3.32206, ASTM B210, ASTM B221, ASTM B241(pipe-seamless), ASTM B345 (pipe-seamless), ASTM B361, ASTM B429, ASTM B483, ASTM B491, MIL G-18014, MIL G-18015, MIL P-25995,MIL W-85, QQ A-200/9, SAE J454, UNS A96063 and HE19.
Temper Types
The most common tempers for 6063 aluminium are: O - Soft, T4-Solution heat treated and naturally aged to a substantially stable condition andT6 - Solution heat treated and artificially aged.
Fabrication
A:Solderability: Good
B:Weldability - Gas: Excellent
C:Weldability - Arc: Excellent
D:Weldability - Resistance: Excellent
E:Brazability: Excellent
F:Workability - Cold: Average
G:Machinability: Average
6063 Aluminum Alloy: Properties
| General Characteristics | |
| Characteristic Appraisal | |
| Strength | Medium |
| Corrosion Resistance | Good |
| Weldability & Brazability | Good |
| Workability | Good |
| Machinability | Fair |
| Chemical Composition | ||
| Element Minimum % Maximum % | ||
| Magnesium | 0.45 | 0.9 |
| Silicon | 0.2 | 0.6 |
| Iron | No Min | 0.35 |
| Copper | No Min | 0.1 |
| Manganese | No Min | 0.1 |
| Chromium | No Min | 0.1 |
| Zinc | No Min | 0.1 |
| Titanium | No Min | 0.1 |
| Other Elements | No Min | 0.05 each, 0.15 in total |
| Physical Properties | |||
| Property 6063-T5 6063-T6 6063-T832 | |||
| Density | 2.70 g/cc | 0.0975 lb/in³ | 2.70 g/cc | 0.0975 lb/in³ | 2.70 g/cc | 0.0975 lb/in³ |
| Mechanical Properties | |||
| Property 6063-T5 6063-T6 6063-T832 | |||
| Tensile Strength | 186 MPa | 27000 psi | 241 MPa | 35000 psi | 290 MPa | 42000 psi |
| Yield Strength | 145 MPa | 21000 psi | 214 MPa | 31000 psi | 269 MPa | 39000 psi |
| Modulus of Elasticity | 68.9 GPa | 10000 ksi | 68.9 GPa | 10000 ksi | 69.0 GPa | 10000 ksi |
| Thermal Properties | |||
| Property | 6063-T5 | 6063-T6 | 6063-T832 |
| Coefficient of Thermal Expansion @20.0 - 100 °C Temp | 21.8 µm/m-°C | 12.1µin/in-°F | 21.8 µm/m-°C | 12.1µin/in-°F | 21.8 µm/m-°C | 12.1µin/in-°F |
| Thermal Conductivity | 209 W/m-K | 1450BTU-in/hr-ft²-°F | 200 W/m-K | 1390BTU-in/hr-ft²-°F | 200 W/m-K | 1390BTU-in/hr-ft²-°F |